|GLASS PASSIVATED JUNCTION TRANSIENT VOLTAGE SUPPRESSOR 5000 Watt Peak Power VOLTAGE to 220 Volts
· Plastic package has Underwriters Laboratory Flammability Classification 94V-O· Glass passivated chip junction in P-600 package· 5000W Peak Pulse Power capability on 10/1000µs waveform· Excellent clamping capability· Low zener impedance· Repetition rate(Duty Cycle):.05%
· Fast response time: typically less than 1.0 ps from 0 volts to BV min· Typical IR less than 1µA above 10V· High temperature soldering guaranteed: seconds/.375" ,(9.5mm) lead length/5lbs., (2.3kg) tension
Case: JEDEC P600 molded plastic Terminals: Axial leads, solderable per MIL-STD-750, Method 2026 Polarity: Color band denoted cathode except Bipolar Mounting Position: Any Weight: 0.07 ounce, 2.1 gram
For Bidirectional use or CA Suffix for types 5KP5.0 thru types 5KP220 Electrical characteristics apply in both directions.
Rating at 25°Cambient temperature unless otherwise specified. Resistive or inductive load, 60Hz. For Capacitive load derate current by 20%.
RATING Peak Power Dissipation TP=1ms(Note 1) Steady State Power Dissipation TL=75°CLead Lengths.375",(9.5mm) (Note 2) Peak Forward Surge Current, 8.3ms Single Half Sine-Wave Superimposed on Rated Load(JECED Method) (Note 3) Operating and Storage Temperature Range
NOTES: 1.Non-repetitive current pulse, per Fig. 3 and derated above TA=25°Cper Fig. 2.Mounted on Copper Leaf area 0.79in2(20mm2). 3.8.3ms single half sine-wave, duty cycle= 4 pulses per minutes maximum.